High-Temperature & Casting
02Key performance
150°CHDT
90MPaFlexural Strength
240cpsViscosity
90Shore DHardness
01
Product overview
概述A consumer-printer heat-resistant grade rated to 150 °C peak and 120 °C continuous without deformation or cracking. Unlike the higher-temperature grades it does not crystallise, so no pre-heating or complex handling is needed, and consumer printers and cure stations deliver its full performance.
- On a consumer cure station, post-cure for 20 minutes or more to reach heat resistance above 120 °C.
03
Applications
应用HTV mouldsSilicone mould masters
150 °C refers to short-term HDT at 0.45 MPa load; 120 °C is the continuous temperature without deformation or cracking
04
Technical data
技术参数| Flexural Strength弯曲强度 | 90MPa |
|---|---|
| Flexural Modulus弯曲弹性模量 | 2800MPa |
| Tensile Strength拉伸强度 | 55MPa |
| Tensile Modulus拉伸弹性模量 | 3100MPa |
| Elongation at Break断裂延伸率 | 4% |
| HDT热变形温度 HDT | 150@0.45 MPa |
| Viscosity粘度 | 240cps |
| Hardness硬度 | 90Shore D |
Values above are the ones documented in our internal data. Nothing is extrapolated. Formal test conditions and standards are stated in the TDS.
05
Printing & post-processing
工艺| Light source适配光源 | 385–405nm LCD / DLP |
|---|---|
| Exposure曝光 | 2–3 s @ 4000–5000 μW/cm² |
| Layer height层厚 | Not provided |
| Post-cure后固化 | Post-cure 20 min+ when service temperature exceeds 120 °C |
Layer height and exposure depend on machine intensity, resin temperature and cross-section; parameters not listed are not recommended.
06 / RELATED
Other materials in this family
XC-HTHR25
High-Temperature Rapid Tooling Resin
耐高温快速模型树脂
280°CHDT
90MPaFlexural Strength
90Shore DHardness
XC-HTHR98
High-Temperature Rapid Tooling Resin 2.0
耐高温快速模型树脂 2.0
180°CHDT
90Shore DHardness
90MPaFlexural Strength
XC-WXCS44
Easy-Cast White Wax
易造白蜡
750°CBurnout Temperature
< 0.1%Ash Content
200cpsViscosity
XRESIN · Sales & engineering
Need a material recommendation, or a sample?
Tell us the service conditions, your printer and the target properties. We will come back with a material recommendation and a starting process window.