High-Temperature & Casting
02Key performance
180°CHDT
90Shore DHardness
90MPaFlexural Strength
3500MPaTensile Modulus
01
Product overview
概述Rated to 180 °C and improved over the previous generation in crystallisation behaviour. Flexural strength stays at 90 MPa and hardness at 90 Shore D, while exposure time drops to 1.5–2 s — a faster route to heat-resistant tooling.
- To reach heat resistance above 180 °C, post-cure thoroughly in a high-energy cure station, or for 30 minutes or more in a consumer unit.
- Before using a printed mould, apply release agent to the cavity and runners for easy demoulding.
03
Applications
应用HTV mouldsSilicone mould mastersInjection mould tooling
180 °C refers to short-term HDT at 0.45 MPa load; continuous service temperature depends on post-cure
04
Technical data
技术参数| Flexural Strength弯曲强度 | 90MPa |
|---|---|
| Flexural Modulus弯曲弹性模量 | 2800MPa |
| Tensile Strength拉伸强度 | 60MPa |
| Tensile Modulus拉伸弹性模量 | 3500MPa |
| Elongation at Break断裂延伸率 | 5% |
| HDT热变形温度 HDT | 180@0.45 MPa |
| Viscosity粘度 | 900cps |
| Hardness硬度 | 90Shore D |
Values above are the ones documented in our internal data. Nothing is extrapolated. Formal test conditions and standards are stated in the TDS.
05
Printing & post-processing
工艺| Light source适配光源 | 385–405nm LCD / DLP |
|---|---|
| Exposure曝光 | 1.5–2 s @ 4000–5000 μW/cm² |
| Layer height层厚 | Not provided |
| Post-cure后固化 | Full cure in a high-energy station, or 30 min+ in a consumer unit |
Layer height and exposure depend on machine intensity, resin temperature and cross-section; parameters not listed are not recommended.
06 / RELATED
Other materials in this family
XRESIN · Sales & engineering
Need a material recommendation, or a sample?
Tell us the service conditions, your printer and the target properties. We will come back with a material recommendation and a starting process window.